- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
Chemical composition and mechanical properties of S235J0 steel plate
The chemical composition and mechanical properties of S235J0 steel plate are as follows:
Chemical composition of S235J0 steel plate (mass percentage) :
- Carbon content (C) : 0.20% Max
- Silicon content (Si) : 0.55% Max
- Manganese content (Mn) : 1.60% Max
- Phosphorus content (P) : maximum 0.040%
- Sulfur content (S) : maximum 0.040%
- Copper content (Cu) : up to 0.55% (when copper content exceeds 0.20%, specified by the supplier)
Mechanical properties of S235J0 steel plate (thickness ≤ 16 mm) :
- Yield strength (ReH) : minimum 235 MPa
- Tensile strength (Rm) : 360-510 MPa
- Elongation (A) : minimum 26%
- Impact toughness (KV) : minimum temperature -20°C, 27 J longitudinal (0°C in welded condition, 27 J transverse)
Please note that the above values are for reference only and the actual values can be adjusted according to different standards and specifications. In addition, the specific properties of steel plates are also affected by factors such as heat treatment process, plate size and shape. In specific applications, reference should be made to the applicable S235J0 steel plate standards and technical specifications to obtain the exact chemical composition and mechanical properties requirements, and to confirm the relevant information of the steel plate with the supplier.