• Improper welding of X80 pipeline may cause cracks
• Brief introduction of API X52 pipeline steel
• The difference between PSL1 and PSL2
• Harm of inclusions in X70 pipeline steel
• API 5L pipeline pipe
• X52 steel plate surface quality standards that need to be met
• The basic production process of API 5L X60 pipeline steel
• The key to Q460D steel welding process
• What does the heat treatment of Q690 Steel include?
• Reasons for choosing Q690D steel

Methods to repair defects of Q345 seamless steel pipe

When there are too many defects in the welded joints of Q345 seamless steel pipes, welding repairs can be used for repairing. Note that the number of times of welding and repairing alloy steel at the same position is not more than 2 times, and the following regulations must be met:
1. Defects must be completely eliminated;
2. When welding Q345 seamless steel pipes, corresponding measures need to be formulated and approved in strict accordance with the requirements of the repair process;
3. Re-appearance inspection and spectral analysis are required after rework;
4. Then heat-treat the joints of Q345 seamless steel pipes;
5. The repair service should carry out the necessary hardness test after the heat treatment of the Q345 seamless steel pipe;
6. After heat treatment, the reworked joint must be consistent with the original process flaw detection again.