- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
301 stainless steel Fatigue Strength
301 is an austenitic stainless steel, with a tensile strength of up to 1800 Mpa, has good resistance to atmospheric corrosion, cold deformation through the processing of steel strength, hardness, and to retain adequate plastic, toughness, combined with the steel in the atmospheric conditions with good resistance to rust,
301 stainless steel Chemical composition:
Cr 16-18%
Ni 6-8%
C 0.15% max
Mn 2% max
Si .75% max
P 0.40% max
S .030% max
301 stainless steel Mechanical properties:
Grade/Temper | Tensile Strength ksi (min.) | Yield Strength 0.2% ksi (min.) | Elongation -% in 50 mm (min.) |
301 1/4 |
125 |
75 |
25 |
301 1/2 |
150 |
110 |
18 |
301 Full Hard |
185 |
140 |
9 |
Impact Resistance:
Annealed austenitic stainless steels exhibit high resistance to impact even at low temperatures. This property, in combination with strength and fabricability, has led to their use in cryogenic applications.
Fatigue Strength:
The endurance limit of annealed Type 301 is 30-45 percent of the tensile strength. Cold rolling increases the endurance limit as compared with annealed material. Stress relieving increases the endurance limit of cold rolled material.
Phone: 0086-18317160019
TEL: 0086-21-61182423
Fax: 0086-21-61182425
E-mail: [email protected]
Skype: shanghai.katalor
Address : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai