- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
ASTM A240 Grade 302 Stainless Steel Wire Hardening
ASTM A240 Grade 302 Stainless Steel Wire is widely found in strip and wire forms. Grade 302 Stainless Steel Wire is a standard specification for chromium and chromium-nickel stainless steelsheet, plate, and strip used for pressure vessels and for general applications. Grade 302 stainless steel wire is widely used in the stamping, spinning and wire forming industry. This alloy is also used to form springs, washers, screens and cables.
ASTM A240 Grade 302 Wire Chemical Composition
Grade |
The Element Max (%) |
||||||
C |
Mn |
P |
S |
Si |
Cr |
Ni |
|
ASTM A240 302 |
0.15 |
2.00 |
0.045 |
0.030 |
0.75 |
17.0-19.0 |
8.0-10 |
Mo |
N |
Cu |
|
|
|
|
|
|
0.10 |
|
|
|
|
|
Mechanical Property of ASTM A240 Grade 302 Stainless Steel
Grade |
ASTM A240 302 Mechanical Property |
||||
Yield |
Tensile |
Elongation |
Hardness, max |
||
ASTM A240 302 |
Min Mpa |
Mpa |
Min % |
Brinell |
Rockwell B |
205 |
515 |
40% |
201 |
92 |
Equivalent steel grade of TP302 Wire
Japan |
USA |
Korea |
Australia |
UK |
Germany |
EU |
France |
JIS |
UNS |
KS |
AS |
BS |
DIN 17440 |
EN |
NFA35-572 |
- |
S30200 |
- |
- |
302S25 |
X12CrNi188 |
- |
Z10CN18.09 |
Grade 302 Stainless Steel Wire Hot Working
Uniform heating to 2100 F(1149 C) will allow Grade 302 stainless steel to be forged, upset and headed successfully. Do not work 302 below 1700 F (927 C).
Grade 302 Stainless Steel Wire Cold Working
Cold working will dramatically increase the hardness of this material, however it is quite ductile and may readily be drawn, spun and upset. Any cold work will cause this alloy to become magnetic.
Grade 302 Stainless Steel Wire Annealing
1850-2050 F (1010-1121 C) with cooling at a rapid rate to avoid the precipitation of chromium carbides.
Grade 302 Stainless Steel Wire Hardening
This alloy does not respond to heat treatment.
Shanghai Katalor Enterprises Co., Ltd is a big complex combined steel stockist whose business related with trade, processing, storage and transportation. we are specialized in supplying ASTM A240 Grade 302 Stainless Steel Wire. We have the good quality and advanced equipment, our products meet the state standard, and also available for customers' requirement. If you have any need of Grade 302 Stainless Steel Wire, please do not hesitate to contact us by email [email protected], we can do our best to help you!