- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
ASTM A240 Grade 310S Stainless Steel Main Material Property List
Alloy 310 is an austenitic stainless steel that combines excellent high temperature properties with good ductility and weld ability. Grade 310S Stainless Steel is mainly used in Furnace Parts, Oil Burner Parts, Heat Exchangers, Welding Filler Wire and Electrodes, Annealing Covers, Combustion Tubes, Fire Box Sheets.
Chemical composition % of grade 310 and 310S stainless steel
Chemical Composition |
310 |
310S |
Carbon |
0.25 max |
0.08 max |
Manganese |
2.00 max |
2.00 max |
Silicon |
1.50 max |
1.50 max |
Phosphorus |
0.045 max |
0.045 max |
Sulphur |
0.030 max |
0.030 max |
Chromium |
24.00 - 26.00 |
24.00 - 26.00 |
Nickel |
19.00 - 22.00 |
19.00 - 22.00 |
Mechanical properties of of grade 310/310S stainless steel
Mechanical Properties |
310/ 310S |
Grade 0.2 % Proof Stress MPa (min) |
205 |
Tensile Strength MPa (min) |
520 |
Elongation % (min) |
40 |
Hardness (HV) (max) |
225 |
Machinability of ASTM A240 Grade 310S
310S Stainless Steel chips are stringy and it will work harden rapidly. It is necessary to keep the tool cutting at all times and use chip breakers.