- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
ASTM A285 Grade C low carbon steel usage
ASTM A285 Grade C is a low to intermediate yield steel used in the fabrication of carbon steel pressure vessels and boilers.
A285 Grade C chemical composition:
Grade |
C |
Si |
Mn |
S |
Al |
Cr |
Cu |
Ni |
Mo |
Nb |
Ti |
V |
285 C |
0.16 |
0.35 |
0.4/1.2 |
0.03 |
0.02 |
0.3 |
0.3 |
0.3 |
0.08 |
0.01 |
0.03 |
0.02 |
A285 Grade C Physical properties:
Grade |
|
A285 grade C |
||
Thickness |
Yield |
Tensile |
Elongation |
|
A285 grade C |
mm |
Min Mpa |
Mpa |
Min % |
6-50 |
205 |
380-515 |
27% |
|
50-200 |
205 |
380-515 |
23% |
A285 Grade C Use:
A285 Grade C is a kind of common carbon steel, whose tensile is low or mid-low. There are three grades or levels material GR A/B/C in the standard ASME SA-285/SA-285M. Plates ordered to this specification A285 Grade C are normally in the as-rolled condition. A285 Grade C may be ordered from the supplier as normalized or stress relieved if so desired. The alloy A285 Grade C is not heat treated for hardening.A285 Grade C is supplied throughout the oil gas and petrochemical industry.The materialA285 Grade C has good forming and welding characteristics under conventional methods.