- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
Duplex stainless steel ASTM 329(S32900)
Stainless steels are classified into martensitic, ferritic and austenitic based on their crystalline structure. In addititon, they form another group known as precipitation-hardened steels, which are a combination of martensitic and austenitic steels.
|
Properties |
Metric |
Imperial |
|
Tensile strength, ultimate |
725 MPa |
105000 psi |
|
Tensile strength, yield (@0.2%) |
550 MPa |
79800 psi |
|
Charpy impact |
54 J |
39.8 ft-lb |
|
Elastic modulus |
190 – 210 GPa |
27557 – 30458 ksi |
|
Poisson’s ratio |
0.27 – 0.30 |
0.27 – 0.30 |
|
Elongation at break (in 50 mm) |
25% |
25% |
|
Hardness, Brinell |
230 |
230 |
|
Hardness, Knoop (converted from Brinell hardness) |
253 |
253 |
|
Hardness, Rockwell B |
96 |
96 |
|
Hardness, Rockwell C (converted from Brinell hardness) |
20 |
20 |
|
Hardness, Vickers (converted from Brinell hardness) |
242 |
242 |
|
Chemical Composition |
|
|
C (Carbon) |
0.08% Max |
|
Fe (Iron) |
Balance |
|
Mn (Manganese) |
1.0% Max |
|
Si (Silicon) |
0.75% Max |
|
S (Sulphur) |
0.03% Max |
|
P (Phosphorus) |
0.04% Max |
|
Cr (Chromium) |
23-28% |
|
Ni (Nickel) |
2.5-5.0% |
|
Mo (Molybdenum) |
1.0-2.0% |
Duplex Stainless Steel 329 was one of the earliest duplex steel which is reflected in its higher permitted carbon content. Its resistance to pitting (PREN about 32) and to crevice corrosion is below that of super duplex steels, therefore use in seawater is limited. Exposure to moderate and high temperature and less rapid cooling may cause embrittlement. Accordingly, design stress values in ASME II do not extend above 260°C for S32900. Impact values are high at room temperature. However, the proportion and orientation of ferrite in welds and base material may significantly affect toughness at subzero temperatures.
Duplex Stainless steel 329 can be used for heat exchangers, chemical tanks, refineries, shafts (marine, etc) pressure vessel parts, flanges, fittings & pipes for the oil and gas industries and offshore technology, paper industry, compressor parts and seawater desalination plants amongst many other applications.
Katalor is one of the preeminent manufacturers and suppliers of Duplex Stainless Steel 329 Round Bars. Immensely useful for construction industries, these bars are offered by us in various sizes and finishes to choose from. Complying the industrial norms, our round bars last for long duration and available in bulk quantities at most reasonable rates.
Phone: 0086-18317160019
TEL: 0086-21-61182423
Fax: 0086-21-61182425
E-mail: [email protected]
Skype: shanghai.katalor
Address : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai