- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
Analysis of A516 steel properties and performance
A516 steel belongs to ordinary carbon steel, and cracks will appear during the rolling process. A516 steel is prone to cold cracking in the steelmaking process, that is, when the slab is heated to a certain temperature and then cooled and then released from the furnace, the inside of the slab is loose.
A516 steel plate belongs to cold crack. In order to eliminate cold cracks, reduce crack defects, and improve rail strength, corrosion resistance and wear resistance, the following measures should be taken when manufacturing automobile sheets:
(1) Use good rolling passes to reduce the content of inclusions in or between plates.
(2) Adopt appropriate heat treatment process conditions and heat treatment system to eliminate cold cracks.
(3) Quenching and tempering treatment is carried out immediately after cold and hot working to improve the strength, hardness, corrosion resistance and wear resistance of the steel.
A516 steel can be made into billets with a thickness of 3~6 mm (width 600~900 mm) by cold rolling or hot rolling. A516 steel is used to manufacture steel plates and spring steel for trucks and other trucks. "Chinese standards stipulate the product quality control requirements for cold-rolled and hot-rolled sheets.