- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
BBN Q345B steel plate rolling process
The heating of Q345B steel plate adopts the "low temperature long-term maintenance" process, and the temperature in the soaking section is reduced by 20 ℃ to 1200 ~ 1220 ℃, so as to avoid the coarsening and growth of slab grains. Prolong the heating time of 30 min in the soaking section to fully promote the diffusion of segregated elements in the billet core.
First of all, formulate a reasonable Q345B steel plate rolling process, increase the pass reduction as much as possible, and ensure that the compactness and grain size of the steel plate in the thickness direction can be uniform; the cumulative reduction rate in the finishing rolling stage is > 50%, so that The body grains can be fully elongated to provide more nucleation particles for ferrite transformation, and the fine ferrite grains are beneficial to the plastic-ductile deformation of Q345B steel plate.
Secondly, in terms of cooling control, it is necessary to formulate a reasonable controlled cooling process for Q345B steel plate. By increasing the cooling rate, the diffusion of supersaturated C atoms can be suppressed, thereby reducing the banded structure in the core of Q345B steel plate.