- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Performance that API 5L X52 PSL2 pipeline steel should have
- Surface Quality Requirements of EH40 Steel plate
- Excellent properties and applications of EH40 shipbuilding Steel
- Influence of gas in 50CrMo4 steel plate
- Cause of Quenching Cracks in 50CrMo4
- Factors Affecting Welding Toughness of
- Z direction performance of EH32 steel plate
- Features of AR450 wear-resistant plate
- Characteristics of NM500 wear-resistant plate
- Harm of inclusions in API 5L X42 pipeline steel
Difference between 12Cr1MoV and 15CrMo steel plate
1. Difference of chemical composition between 12Cr1MoV and 15CrMo steel plate:
Chemical composition of 12Cr1MoV steel plate: C: 0.08-0.15, Si: 0.17-0.37, Mn: 0.40-0.70, Cr: 0.90-1.2, Mo: 0.25-0.35, V: 0.15-0.30.
15CrMo steel plate chemical composition:
C 0.12-0.18%, Si 0.17-0.37%, Mn 0.40-0.70%, Cr 0.80-1.10%, Mo 0.40-0.55%.
2. Differences in mechanical properties between 12Cr1MoV and 15CrMo steel plate:
Mechanical properties of 12Cr1MoV steel plate: tensile strength (σb/MPa): ≥ 490, yield point (σs/MPa): ≥ 245, elongation after fracture (δ5/%): ≥ 22, reduction of area (ψ/%): ≥ 50, impact absorption work (Aku2/J): ≥ 71, brinell hardness (HBS100/3000) (annealed or tempered at high temperature): ≤ 179.
The mechanical properties of 15CrMo steel plate are as follows:
Tensile strength: 440 MPa; yield strength: 295 MPa; elongation after fracture: 22%; shrinkage after fracture: 60%; impact absorption energy: 94 J.