Contact us
- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
HOT News
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
Difference between P690QL1 and P690QL2 steel plate
Posted:2022-01-20 11:32:37
The difference between P690QL1 and P690QL2 steel plate is that the impact temperature is different. The impact temperature of the P690QL1 steel plate is -40℃, and the P690QL2 steel plate is -60℃. It is a fine-grained steel that can be quenched and tempered. The size, shape and allowable deviation of the steel plate shall meet the requirements of 2007+A1:2009 in EN10028-1. P690QL2 steel plate is steel for pressure equipment, with good plasticity, toughness, cold bending performance and welding performance.
Chemical composition and melting analysis of P690QL1 and P690QL2 steel plate:
Composition Notes: The proportion of grain refining elements should be at least 0.015. Aluminum is also included in these elements, Als≥0.015, Alt≥0.018.
Mechanical properties of P690QL1 steel plate:
Mechanical properties of P690QL2 steel plate:
Chemical composition and melting analysis of P690QL1 and P690QL2 steel plate:
C | Si | Mn | P | S | Ni | Cr | Mo | Cu | Nb | V | Ti | N | Zr | B |
≤0.2 | ≤0.8 | ≤1.7 | ≤0.02 | ≤0.010 | ≤2.5 | ≤1.5 | ≤0.7 | ≤0.3 | ≤0.06 | ≤0.12 | ≤0.05 | ≤0.015 | ≤0.15 | ≤0.005 |
Composition Notes: The proportion of grain refining elements should be at least 0.015. Aluminum is also included in these elements, Als≥0.015, Alt≥0.018.
Mechanical properties of P690QL1 steel plate:
Delivery Status | Thickness (mm) | Mechanical properties | |
Quenching and tempering | <5 | ReH(MPa) | ≥690 |
Rm(MPa) | 770-940 | ||
A(%) | ≥14 | ||
5-50 | ReH(MPa) | ≥690 | |
Rm(MPa) | 770-940 | ||
A(%) | ≥14 | ||
Impact temperature | -40 | ||
Akv(J) | ≥27 | ||
>50-100 | ReH(MPa) | ≥670 | |
Rm(MPa) | 770-940 | ||
A(%) | ≥14 | ||
Impact temperature | -40 | ||
Akv(J) | ≥27 | ||
>100-150 | ReH(MPa) | ≥630 | |
Rm(MPa) | 720-900 | ||
A(%) | ≥14 | ||
Impact temperature | -40 | ||
Akv(J) | ≥27 |
Mechanical properties of P690QL2 steel plate:
Delivery Status | Thickness (mm) | Mechanical properties | |
Quenching and tempering | <5 | ReH(MPa) | ≥690 |
Rm(MPa) | 770-940 | ||
A(%) | ≥14 | ||
5-50 | ReH(MPa) | ≥690 | |
Rm(MPa) | 770-940 | ||
A(%) | ≥14 | ||
Impact temperature | -60 | ||
Akv(J) | ≥27 | ||
>50-100 | ReH(MPa) | ≥670 | |
Rm(MPa) | 770-940 | ||
A(%) | ≥14 | ||
Impact temperature | -60 | ||
Akv(J) | ≥27 | ||
>100-150 | ReH(MPa) | ≥630 | |
Rm(MPa) | 720-900 | ||
A(%) | ≥14 | ||
Impact temperature | -60 | ||
Akv(J) | ≥27 |