Contact us
- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
HOT News
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
Heat treatment process of SPV490Q steel plate
Posted:2021-10-16 15:32:05
Analysis on the influence of heat treatment process of SPV490Q steel plate:
1. The SPV490Q steel plate produced by the direct quenching process has good strength and toughness matching. This process can replace the traditional offline modulation process to achieve the purpose of saving energy and reducing costs.
2. The strength of the directly quenched SPV490Q steel plate after tempering is relatively small, and the toughness is improved obviously; When the quenched steel plate is reheated for tempering, the strength will be greatly reduced. With the improvement of toughness and plasticity, the former has better tempering resistance.
3. The martensitic laths of high dislocation density lath martensite obtained by direct quenching are fine, bent and crossed with each other. After reheating the quenched steel, the martensite structure with low dislocation density and coarse martensite lath are obtained.
4. Under the same tempering conditions, the carbides precipitated by directly quenching SPV490Q steel plates are fine and dispersed, while the carbides precipitated by reheating and quenching steel plates are relatively coarse.
1. The SPV490Q steel plate produced by the direct quenching process has good strength and toughness matching. This process can replace the traditional offline modulation process to achieve the purpose of saving energy and reducing costs.
2. The strength of the directly quenched SPV490Q steel plate after tempering is relatively small, and the toughness is improved obviously; When the quenched steel plate is reheated for tempering, the strength will be greatly reduced. With the improvement of toughness and plasticity, the former has better tempering resistance.
3. The martensitic laths of high dislocation density lath martensite obtained by direct quenching are fine, bent and crossed with each other. After reheating the quenched steel, the martensite structure with low dislocation density and coarse martensite lath are obtained.
4. Under the same tempering conditions, the carbides precipitated by directly quenching SPV490Q steel plates are fine and dispersed, while the carbides precipitated by reheating and quenching steel plates are relatively coarse.