Contact us
- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
HOT News
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
High strength 20CrMnMo steel chemical composition
Posted:2021-12-23 15:30:00
20CrMnMo steel is high-strength advanced carburizing steel. Its strength is higher than 15CrMnMo, plasticity and toughness are slightly lower, hardenability and mechanical properties are higher than 20CrMnTi. After quenching and tempering, 20CrMnMo steel has good comprehensive mechanical properties and low temperature impact toughness.
Chemical composition and melting analysis of 20CrMnMo steel sheet:
20CrMnMo steel has high bending strength and wear resistance after carburizing and quenching, but it is prone to cracks during grinding. 20CrMnMo steel weldability is not good, and it is suitable for resistance welding. Preheating is required before welding, and tempering treatment after welding.
Chemical composition and melting analysis of 20CrMnMo steel sheet:
Grade | C | Si | Mn | P | S | Cr | Mo | Cu |
20CrMnMo | 0.17-0.23 | 0.17-0.37 | 0.9-1.2 | ≤0.03 | ≤0.03 | 1.1-1.4 | 0.2-0.3 | ≤0.25 |
20CrMnMo steel has high bending strength and wear resistance after carburizing and quenching, but it is prone to cracks during grinding. 20CrMnMo steel weldability is not good, and it is suitable for resistance welding. Preheating is required before welding, and tempering treatment after welding.