Contact us
- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
HOT News
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
Q550F steel plate for high-strength structure
Posted:2021-12-25 09:07:05
Melting analysis of chemical composition of Q550F steel plate:
Composition Remarks: At least one grain refinement element of Nb, Ti, V, Al is added to the steel, and the minimum amount of at least one element is 0.015 (Als for Al). Alt can be used instead of Als, in this case Alt ≥ 0.018. Ceq = C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15
Mechanical properties of Q550F steel plate:
Q550F steel plate executive standard: GB/T 16270.
Q550F steel plate delivery status: quenching + tempering.
Q550F steel plate application range:
Q550F quenched and tempered steel plate for high-strength structure, used to manufacture steel structural parts such as coal mine hydraulic supports, heavy vehicles, construction machinery, and wear-resistant structures that require good weldability.
Grade | C | Si | Mn | P | S | Ni |
Q550F | ≤0.2 | ≤0.8 | ≤1.7 | ≤0.02 | ≤0.010 | ≤2 |
Cr | Mo | Cu | Nb | V | Ti | B |
≤1.5 | ≤0.7 | ≤0.5 | ≤0.06 | ≤0.12 | ≤0.05 | ≤0.005 |
Composition Remarks: At least one grain refinement element of Nb, Ti, V, Al is added to the steel, and the minimum amount of at least one element is 0.015 (Als for Al). Alt can be used instead of Als, in this case Alt ≥ 0.018. Ceq = C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15
Mechanical properties of Q550F steel plate:
Thickness | Mechanical properties | ||
≤50mm | ReH(MPa) | ≥550 | When the yield is not obvious, use Rp0.2 |
Rm(MPa) | 640-820 | ||
A(%) | ≥16 | ||
Impact temperature | -60 | ||
Akv(J) | ≥34 | Longitudinal | |
>50-100mm | ReH(MPa) | ≥530 | When the yield is not obvious, use Rp0.2 |
Rm(MPa) | 640-820 | ||
A(%) | ≥16 | ||
Impact temperature | -60 | ||
Akv(J) | ≥34 | Longitudinal | |
>100-150mm | ReH(MPa) | ≥490 | When the yield is not obvious, use Rp0.2 |
Rm(MPa) | 590-770 | ||
A(%) | ≥16 | ||
Impact temperature | -60 | ||
Akv(J) | ≥34 | Longitudinal |
Q550F steel plate executive standard: GB/T 16270.
Q550F steel plate delivery status: quenching + tempering.
Q550F steel plate application range:
Q550F quenched and tempered steel plate for high-strength structure, used to manufacture steel structural parts such as coal mine hydraulic supports, heavy vehicles, construction machinery, and wear-resistant structures that require good weldability.