Contact us
- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
HOT News
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
Quenched and tempered 07MnNiVDR high-strength steel plate for pressure vessel
Posted:2021-05-20 17:23:15
07MnNiVDR is a low welding crack susceptibility steel. It is a quenched and tempered high-strength steel plate for pressure vessels with a thickness of 10mm-60mm. 07MnNiVDR high-strength steel is widely used in high-end technical fields such as petroleum, chemical industry, power stations, and boilers to make reactors, heat exchangers, high-tech products such as separators, spherical tanks, and oil and gas tanks.
07MnNiVDR high-strength steel chemical composition requirements: C≤0.09, Si 0.15-0.4, Mn 1.2-1.6, P≤0.018, S≤0.008, Cu≤0.25, Ni 0.2-0.5, Cr≤0.3, Mo≤0.3, V 0.02-0.06, B ≤0.002, Pcm≤0.21.
07MnNiVDR steel plate mechanical performance requirements:
Yield strength (MPa) ≥490
Tensile strength (MPa) 610-730
Elongation A(%)≥17
07MnNiVDR steel plates should be delivered in the quenched and tempered heat treatment state, where the tempering temperature is greater than 600 degrees.