301 stainless steel Machinability ,301 stainless steel Welding

301 stainless steel is an austenitic stainless steel capable of attaining high strengths and ductility by cold working. It is not hardenable by heat treatment.

301 stainless steel is non-magnetic in the annealed condition and becomes increasingly magnetic with cold working. It is preferable over types 302 and 304 in the tempered condition because the higher enlongations (which are attainable at a given strength level) facilitate fabrication.

301 stainless steel Chemistry Composition
Carbon: 0.15 max
Manganese: 2.00 max
Silicon: 1.00 max
Chromium: 16.00- 18.00
Nickel: 6.00- 8.00
Aluminum: 0.75 max
Phosphorus: 0.040 max
Sulphur: 0.030 max
Copper: 0.75 max
Nitrogen: 0.10 max
Iron: Balance

301 stainless steel Machinability
301 is not available in bar, plate, tube, pipe or forging, therefore no information is available.

301 stainless steel Welding
All popular techniques may be used, however the material will lose temper in the heat affected weld zone.

301 stainless steel Corrosion Resistance
301 has good corrosion resistance and is used in many food service applications, similar to grade 304.

as a 301 stainless steel exporter , more information about 301 stainless steel Machinability or 301 stainless steel Welding , please contact us!