ASTM A283 Gr A,B,C,D Low and Intermediate Tensile Strength Carbon Steel Plates

Posted:2016-11-30 22:35:33

ASTM A283 Gr A,B,C,D steel specification covers four grades of low carbon steel plates of structural quality for general application. Grades A, B, C and D.
ASTM A283 Gr A,B,C,D Low and Intermediate Tensile Strength Carbon Steel Plates Chemical Properties

Grade A

Grade B

Grade C

Grade D

Carbon, max

0.14

0.17

0.24

0.27

Manganese, max

0.90

0.90

0.90

0.90

Phosphorus, max

0.035

0.035

0.035

0.035

Sulphur, max

0.04

0.04

0.04

0.04

Silicon
Plates 1 1/2 in and under, max
Plates over 1 1/2 in

0.40
0.15-0.40

0.40
0.15-0.40

0.40
0.15-0.40

0.40
0.15-0.40

Copper min % when copper steel is specified

0.20

0.20

0.20

0.20

ASTM A283 Gr A,B,C,D Low and Intermediate Tensile Strength Carbon Steel Plates Mechanical Properties

Grade A

Grade B

Grade C

Grade D

Tensile Strength:

45,000 -60,000 psi
[310 - 415 MPa]

50,000 -65,000 psi
[345 - 450 MPa]

55,000 75,000 psi
[380 - 515 MPa]

60,000 -80,000 psi
[415 - 550 MPa]

Min. Yield Point:

24,000psi
[165 MPa]

27,000psi
[185 MPa]

30,000psi
[205 MPa]

33,000psi
[230 MPa]

Elongation in 8":

27% min

25% min

22% min

20% min

Elongation in 2":

38% min

28% min

25% min

23% min

Katalor steel as a steel factory in China,offer all kinds of specification ASTM A283 Gr A,B,C,D Low and Intermediate Tensile Strength Carbon Steel Plates,if you need ASTM A283 Gr A,B,C,D steel,contact us now!


InquiryPlease feel free to give your inquiry in the form below. we will reply you quickly!
Name: *
E-mail: *
Country: *
Tel:
 
Company:
Language:
Product: steel plate steel pipe shipbuilding steel
Message: Please enter details such as Material, Specification, Quantity, Port, other requirments !
 
Copyright © 2011 by Shanghai Katalor Enterprises Co., Ltd. All rights reserved