- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
Steel plate for for Boiler Pressure Vessel EN 10028-2 P355GH steel
P355GH steel is a carbon steel alloy engineered for use in pressurised service. It is used as a weldable material in the fabrication of pressure vessels and industrial boilers which are commonly found in petrochemical plants, oil refineries and gas installations.
P355GH steel is an ideal material for use in pressure vessels, especially in the storage of hot liquids. It is produced under the Euro Norm standard EN10028 which replaced the older British and German DIN standards. The material is an equivalent to the American standard grades ASTM A516 Grade 70 and ASME SA516 Grade 70.
It is a normailized steel which is designed for use in elevated temperatures. The material shows good tensile and yield strength and has good welding characteristics when using conventional welding methods. This particular grade also offers good cold and hot forming properties.
Normalization improves the toughness of the steel. It is an annealing process where the material is heated and left to cool naturally. The method essentially toughens and hardens the steel providing increased tensile strength. P335GH steel pressure vessel is delivered in a normalized condition.
The EN10028 standard specifically covers steels for use in steel vessels and boilers and grades vary dependent on the tensile and yield characteristics of the steel. P355GH steel offers a range of tensile strength from 510 to 630 MPa dependent on thickness and yield strength range of 280 to 355 MPa.
P355GH steel Chemical analysis -% by mass* (max)
Grade | C. % | Mn.% | S. | N | Cu | Nb | Ti. | Si. | P. | AL | Cr. | Mo. | Ni | Vi |
P355GH | 0.10-0.22 | 0.10-1.70 | 0.015 | 0.012 | 0.30 | 0.020 | 0.03 | 0.60 | 0.025 | 0.020 | 0.30 | 0.08 | 0.30 | 0.02 |
P355GH steel Mechanical properties
Grade | Type | Thickness mm | Yield strength Mpa(min) | Tensile Strength MPa | Elongation % (min) | Impact Energy (KVJ) (min) | ||
-20° | 0° | +20 | ||||||
P355GH | Normalized | ≤16 16>to≤40 40>to≤60 60>to≤100 100>to≤150 150>to≤250 | 355 | 510-650 | 20 | 27 | 34 | 40 |
345 | 510-650 | 20 | 27 | 34 | 40 | |||
335 | 460-580 | 20 | 27 | 34 | 40 | |||
315 | 490-630 | 20 | 27 | 34 | 40 | |||
295 | 480-630 | 20 | 27 | 34 | 40 | |||
280 | 470-630 | 20 | 27 | 34 | 40 |