Contact us
- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
HOT News
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
Heat treatment of submarine steel
Posted:2021-06-01 11:26:00
In order to improve the comprehensive properties of submarine steel and give full play to its performance potential, submarine steel is usually quenched and tempered.
Before 1960s, pressure quenching machine and high-pressure water cooling were used to obtain low-carbon martensite, and then tempered to obtain tempered martensite with good comprehensive properties. But in this way, the steel plate is easy to deform and its properties are not uniform; Since the 1970s, the quenching process has been changed to the radiation press quenching machine without oxidation heating, which not only solves the uniformity of steel plate performance, but also improves the deformation of steel plate, and obtains the steel plate with good shape. The holding time of quenching heating is usually 23min / mm, the holding time of tempering is usually 58min / mm, and the quenching temperature is about 900℃.
Before 1960s, pressure quenching machine and high-pressure water cooling were used to obtain low-carbon martensite, and then tempered to obtain tempered martensite with good comprehensive properties. But in this way, the steel plate is easy to deform and its properties are not uniform; Since the 1970s, the quenching process has been changed to the radiation press quenching machine without oxidation heating, which not only solves the uniformity of steel plate performance, but also improves the deformation of steel plate, and obtains the steel plate with good shape. The holding time of quenching heating is usually 23min / mm, the holding time of tempering is usually 58min / mm, and the quenching temperature is about 900℃.