- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Improper welding of X80 pipeline may cause cracks
- Brief introduction of API X52 pipeline steel
- The difference between PSL1 and PSL2
- Harm of inclusions in X70 pipeline steel
- API 5L pipeline pipe
- X52 steel plate surface quality standards that need to be met
- The basic production process of API 5L X60 pipeline steel
- The key to Q460D steel welding process
- What does the heat treatment of Q690 Steel include?
- Reasons for choosing Q690D steel
EN10155 S355J2WP
S355J2WP,S355J2WP steel plate,EN S355J2WP steel,EN10155 S355J2WP steel plate/sheet, EN10155 S355J2WP steel plate/sheet for atmospheric corrosion resistance, S355J2WP carbon steel used for resisting atmospheric corrosion , EN10155 S355J2WP steel plate for atmospheric corrosion resistance,S355J2WP steel supplier
/Chinese supplier, S355J2WP steel price...
Equivalent grade :
S355J2WP steel plate/sheet is in EN10155 standard. It's grade Number is 1.8946. The equal material of S355J2WP is: NFA 35-502 E36W4, UNI Fe510D1K1, ASTM A242 Type 1
|
S355J2WP |
ASTM |
A242 Type 1 |
|
NFA 35-502 |
E36W4 |
|
|
UNI |
Fe510D1K1 |
EN10155 S355J2WP steel Chemical Composition
Main chemical composition in EN10155 S355J2WP steel : Carbon: max 0.12 , Manganese max 1.00 , Silicon max 0.75 , Sulphur max 0.03, Phosphorus from 0.06-0.15 , More detailed information, please refer to the flowing table:
|
C % |
Mn % |
Cr % |
Si % |
CEV % |
S % |
|
Max 0.12 |
Max 1 |
0.3-1.25 |
Max 0.75 |
Max 0.52 |
Max 0.03 |
|
Cu % |
P % |
|
|
|
|
|
0.25-0.55 |
0.06 - 0.15 |
|
|
|
|
Method of deoxidation FF = fully killed steel
CEV= C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15
For long products the P and S content can be 0.005% higher
The S355J2WP steels may show a Ni content of max. 0,65 %
The S355J2WP steels shall contain at least one of the following elements: Al total ≥ 0,020 %, Nb: 0,015 - 0,060 %, V: 0,02 - 0,12 %, Ti: 0,02 - 0,10 %. If these elements are used in combination, at least one of them shall be present with the minimum content indicated.
EN10155 S355J2WP steel Mechanical Properties
If S355J2WP mechanical properties have been significantly modified by heavy coldforming, either stress relief annealing or normalised may be applied. Normalised should also be applied following hotforming outside of the temperature range of 750 - 1.050 °C and after overheating. The tensile test values given in the table apply to longitudinal samples; in case of strip and sheet steel of widths of ≥600 mm they apply to transverse samples.
|
Grade |
Min. Yield Strength Mpa |
Tensile Strength MPa |
Impact |
||||||||
|
S355J2WP |
Nominal Thickness (mm) |
Nominal Thickness (mm) |
degree |
J |
|||||||
|
Thick mm |
≤16 |
>16 |
>40 |
>63 |
>80 |
>100 |
≤3 |
>3 ≤100 |
>100 ≤150 |
-20 |
27 |
|
S355J2WP |
355 |
345 |
…. |
…. |
…. |
…. |
510-680 |
470-630 |
…. |
||
Shanghai katalor industry Co.,Ltd will return you with high-quality products and complete after-sale service with the lowest price. we commite to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development.As S355J2WP Mechanical and S355J2WP suppliers,we can supply S355J2WP Chemical,S355J2WP Mechanical and S355J2WP standard for you ,please click to contact us